PA66 L IMP NATURAL
0
- Properties:Improved impact resistancegood impact resistance
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 1.5 | ||
| Water absorption rate | ISO 62 | 0.20 % | |
| Shrinkage rate | ISO 294-4 | 2.0 % | |
| density | ISO 1183 | 1.08 到 1.10 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Supporting hardness | ISO 868 | 75 到 78 | |
| Flexural modulus | ISO 178 | 1900 到 2100 MPa | |
| bending strength | ISO 178 | 65.0 到 75.0 MPa | |
| Tensile modulus | ISO 527-2 | 2300 到 2400 MPa | |
| Tensile stress | ISO 527-2 | 55.0 到 65.0 MPa | |
| Tensile strain | ISO 527-2 | 30 到 50 % | |
| Charpy Notched Impact Strength | ISO 179/1eA | 15 到 30 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 15 到 30 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75-2/B | 200 ℃ | ||
| ISO 75-2/A | 75.0 | ||
| vicat | ISO 306/B | 230 ℃ | |
| ISO 3146 | 240 到 260 ℃ | ||
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.