Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 L IMP NATURAL EPSAN TURKEY
--
--
Improved impact resistance, good impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | EPSAN TURKEY/L IMP NATURAL |
|---|---|---|---|
| bending strength | 23℃ | ISO 178 | 65.0 to 75.0 MPa |
| tensile strength | 断裂, 23℃ | ISO 527-2 | 55.0 to 65.0 MPa |
| Shore hardness | 支撐 D | ISO 868 | 75 to 78 |
| Flexural modulus | 23℃ | ISO 178 | 1900 to 2100 MPa |
| Tensile modulus | 23℃ | ISO 527-2 | 2300 to 2400 MPa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 15 to 30 kJ/m² |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 30 to 50 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 15 to 30 kJ/m² |
| physical property | Test Condition | Test Method | EPSAN TURKEY/L IMP NATURAL |
|---|---|---|---|
| Shrinkage rate | TD: 3.00 mm | ISO 294-4 | 2.0 % |
| Water absorption rate | 饱和, 23℃ | ISO 62 | 0.20 % |
| density | ISO 1183 | 1.08 to 1.10 g/cm³ | |
| Shrinkage rate | MD: 3.00 mm | 1.5 |
| Thermal performance | Test Condition | Test Method | EPSAN TURKEY/L IMP NATURAL |
|---|---|---|---|
| melting temperature | ISO 3146 | 240 to 260 ℃ | |
| vicat | ISO 306/B | 230 ℃ | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 200 ℃ |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 75.0 |