Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.41 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 11 g/10min |
| Shrinkage rate | | ASTM D955 | 0.0-0.20 % |
| Shrinkage rate | | ASTM D955 | 1.4-1.6 % |
| Water absorption rate | | ASTM D570 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 106 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | ASTM D3835 | 450 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 223 Mpa |
| elongation | | ASTM D638 | 1.7 % |
| elongation | | ISO 527-2/1A/5 | 1.7 % |
| Flexural modulus | | ASTM D790 | 17900 Mpa |
| Flexural modulus | | ISO 178 | 21500 Mpa |
| bending strength | | ASTM D790 | 321 Mpa |
| bending strength | | ISO 178 | 319 Mpa |
| compressive strength | | ASTM D695 | 188 Mpa |
| shear strength | | ASTM D732 | 103 Mpa |
| Tensile modulus | | ASTM D638 | 20900 Mpa |
| Tensile modulus | | ISO 527-2/1A/1 | 25400 Mpa |
| tensile strength | | ISO 527-2/1A/5 | 218 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 64 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 8.5 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 640 J/m |
| Suspended wall beam without notch impact strength | | ISO 180 | 43 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 315 °C |
| Glass Transition Temperature | | ASTM D3418 | 147 °C |
| melting temperature | | ASTM D3418 | 343 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 6.7E-06 cm/cm/°C |
| specific heat | | DSC | 1310 J/kg/°C |
| specific heat | | DSC | 1810 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.37 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.