PEEK KT-880 CF30 SOLVAY USA
KETASPIRE®
Electrical field、Electronic field、Industrial applications
Chemical resistance、Fatigue resistance、heat-resisting、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -- | ISO 180 | 8.5 kJ/m² |
| Suspended wall beam without notch impact strength | -- | ASTM D4812 | 640 J/m |
| Impact strength of cantilever beam gap | -- | ASTM D256 | 64 J/m |
| Suspended wall beam without notch impact strength | -- | ISO 180 | 43 kJ/m² |
| hardness | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 106 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| elongation | 断裂5 | ASTM D638 | 1.7 % |
| Tensile modulus | -- | ISO 527-2/1A/1 | 25400 Mpa |
| tensile strength | -- | ASTM D638 | 223 Mpa |
| bending strength | -- | ASTM D790 | 321 Mpa |
| Tensile modulus | -- | ASTM D638 | 20900 Mpa |
| Flexural modulus | -- | ISO 178 | 21500 Mpa |
| elongation | 断裂 | ISO 527-2/1A/5 | 1.7 % |
| bending strength | -- | ISO 178 | 319 Mpa |
| shear strength | ASTM D732 | 103 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/5 | 218 Mpa |
| Flexural modulus | -- | ASTM D790 | 17900 Mpa |
| compressive strength | ASTM D695 | 188 Mpa |
| flammability | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| melt viscosity | 400°C,1000sec^-1 | ASTM D3835 | 450 Pa·s |
| physical property | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| melt mass-flow rate | 400°C/2.16kg | ASTM D1238 | 11 g/10min |
| Shrinkage rate | TD:3.18mm | ASTM D955 | 1.4-1.6 % |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| Shrinkage rate | MD:3.18mm | ASTM D955 | 0.0-0.20 % |
| density | ASTM D792 | 1.41 g/cm³ |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/KT-880 CF30 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-50到50°C | ASTME831 | 6.7E-06 cm/cm/°C |
| specific heat | 50°C | DSC | 1310 J/kg/°C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ASTM D648 | 315 °C |
| thermal conductivity | ASTMC177 | 0.37 W/m/K | |
| specific heat | 200°C | DSC | 1810 J/kg/°C |
| melting temperature | ASTM D3418 | 343 °C | |
| Glass Transition Temperature | ASTM D3418 | 147 °C |