Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| density | | ISO 1183 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238, ISO 1133 | 5.0 g/10 min |
| Shrinkage rate | | ASTM D955 | 0.50 到 0.70 % |
| Shrinkage rate | | ISO 2577 | 0.50 到 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 122 |
| Rockwell hardness | | ISO 2039-2 | 122 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | > 88.0 % |
| Haze ratio | | ASTM D1003 | < 2.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638, ISO 527-2 | 70.0 Mpa |
| Flexural modulus | | ASTM D790, ISO 178 | 2040 Mpa |
| bending strength | | ASTM D790, ISO 178 | 100 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 780 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648, ISO 75-2/A | 127 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.