| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 780 J/m |
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| Rockwell hardness | R 级, 23°C | ASTM D785 | 122 |
| R 计秤, 23°C | ISO 2039-2 | 122 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| Flexural modulus | 23°C | ASTM D790, ISO 178 | 2040 Mpa |
| tensile strength | 23°C | ASTM D638, ISO 527-2 | 70.0 Mpa |
| bending strength | 23°C | ASTM D790, ISO 178 | 100 Mpa |
| optical performance | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| transmissivity | 1000 µm | ASTM D1003 | > 88.0 % |
| Haze ratio | 1000 µm | ASTM D1003 | < 2.0 % |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm, All Colors | UL 94 | V-0 |
| 1.0 mm, All Colors | UL 94 | V-0 | |
| 1.2 mm, All Colors | UL 94 | V-0 | |
| 3.0 mm, All Colors | UL 94 | V-0 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.50 到 0.70 % |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Shrinkage rate | 3.20 mm | ISO 2577 | 0.50 到 0.70 % |
| density | -- | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238, ISO 1133 | 5.0 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC3832 |
|---|---|---|---|
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.18 mm | ASTM D648, ISO 75-2/A | 127 °C |