Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ISO1183 | 1.11 g/cm³ |
| 收缩率 | TD | ISO294-4 | 1.7 % |
| 收缩率 | MD | ISO294-4 | 1.7 % |
| 吸水率 | 23°C,24hr | ISO62 | 0.90 % |
| 顶出温度 | | | 190 °C |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 187 °C |
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 65.0 °C |
| 熔融温度 | | ISO11357-3 | 262 °C |
| 线性热膨胀系数 | MD | ISO11359-2 | 1E-04 cm/cm/°C |
| 线性热膨胀系数 | TD | ISO11359-2 | 1E-04 cm/cm/°C |
| 补充信息 | Test Condition | Test Method | Test Result |
|---|
| EmissionofOrganicCompounds | | VDA277 | 10.0 µgC/g |
| Odor | | VDA270 | 4.00 |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| 燃烧速率3 | 1.00mm | ISO3795 | 29 mm/min |
| UL阻燃等级 | 0.8mm | UL94 | HB |
| UL阻燃等级 | 1.5mm | UL94 | HB |
| UL阻燃等级 | 0.8mm | IEC60695-11-10,-20 | HB |
| UL阻燃等级 | 1.5mm | IEC60695-11-10,-20 | HB |
| FMVSS可燃性 | | FMVSS302 | B |
| Fogging-G-value | condensate | ISO6452 | 1E-04 g |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 | | ISO527-2 | 2400 Mpa |
| 拉伸应力 | 屈服 | ISO527-2 | 61.0 Mpa |
| 拉伸应变 | 屈服 | ISO527-2 | 5.0 % |
| 标称拉伸断裂应变 | | ISO527-2 | 25 % |
| 弯曲模量 | | ISO178 | 2200 Mpa |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 表面电阻率 | | IEC60093 | -- ohms |
| 体积电阻率 | | IEC60093 | >1.0E+15 ohms·cm |
| 相对电容率 | 100Hz | IEC60250 | 3.90 |
| 相对电容率 | 1MHz | IEC60250 | 3.70 |
| 耗散因数 | 100Hz | IEC60250 | 6E-03 |
| 耗散因数 | 1MHz | IEC60250 | 0.013 |
| 漏电起痕指数 | | IEC60112 | 600 V |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 简支梁缺口冲击强度 | -40°C | ISO179/1eA | 12 kJ/m² |
| 简支梁缺口冲击强度 | 23°C | ISO179/1eA | 19 kJ/m² |
| 悬壁梁缺口冲击强度 | -40°C | ISO180/1A | 11 kJ/m² |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 13 kJ/m² |
| 悬壁梁缺口冲击强度 | 23°C | ISO180/1A | 17 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices