PA66 MT409AHS GY DUPONT USA
Zytel®
Electrical appliances、Automotive sector、Electrical field、Electronic field
Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 187 °C |
| 1.8MPa,未退火 | ISO75-2/A | 65.0 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1E-04 cm/cm/°C |
| Melting Temperature | ISO11357-3 | 262 °C |
| Additional | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 10.0 µgC/g | |
| Odor | VDA270 | 4.00 |
| Physical | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.11 g/cm³ | |
| Modeling Shrinkage | TD | ISO294-4 | 1.7 % |
| Ejection Temperature | 190 °C | ||
| Modeling Shrinkage | MD | ISO294-4 | 1.7 % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.90 % |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2200 Mpa | |
| Tensile Strain | 屈服 | ISO527-2 | 5.0 % |
| Tensile Stress | 屈服 | ISO527-2 | 61.0 Mpa |
| Nominal Tensile Strain at Break | ISO527-2 | 25 % | |
| Tensile Modulus | ISO527-2 | 2400 Mpa |
| Impact Properties | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 13 kJ/m² |
| -40°C | ISO180/1A | 11 kJ/m² | |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 12 kJ/m² |
| 23°C | ISO179/1eA | 19 kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 17 kJ/m² |
| Flammability | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | 29 mm/min |
| Flame Rating | 1.5mm | IEC60695-11-10,-20 | HB |
| 0.8mm | IEC60695-11-10,-20 | HB | |
| Fogging-G-value | condensate | ISO6452 | 1E-04 g |
| Flame Rating | 0.8mm | UL94 | HB |
| 1.5mm | UL94 | HB | |
| FMVSS Flammability | FMVSS302 | B |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/MT409AHS GY |
|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.90 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.013 |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 600 V | |
| Surface Resistivity | IEC60093 | -- ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 3.70 |
| Dissipation Factor? | 100Hz | IEC60250 | 6E-03 |