LDPE Petrothene® NA373244
0
- Usages:Thin filmcast film
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D1505 | 0.924 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 3.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 70 | |
| ASTM D2457 | 77 | ||
| Haze ratio | ASTM D1003 | 5.4 % | |
| ASTM D1003 | 3.4 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elmendorf tear strength | ASTM D1922 | 170 g | |
| ASTM D1922 | 160 g | ||
| tensile strength | ASTM D882 | 18.6 MPa | |
| ASTM D882 | 29.1 MPa | ||
| ASTM D882 | 17.2 MPa | ||
| ASTM D882 | 17.0 MPa | ||
| elongation | ASTM D882 | 200 % | |
| ASTM D882 | 230 % | ||
| Tensile strain | ASTM D882 | 500 % | |
| film thickness | 32 µm | ||
| Secant modulus | ASTM D882 | 159 MPa | |
| ASTM D882 | 208 MPa | ||
| Dart impact | ASTM D1709 | 110 g | |
| Elmendorf tear strength | ASTM D1922 | 270 g | |
| ASTM D1922 | 300 g | ||
| Secant modulus | ASTM D882 | 172 MPa | |
| ASTM D882 | 197 MPa | ||
| tensile strength | ASTM D882 | 10.9 MPa | |
| ASTM D882 | 9.38 MPa | ||
| ASTM D882 | 10.7 MPa | ||
| ASTM D882 | 9.31 MPa | ||
| Tensile strain | ASTM D882 | 610 % | |
| Dart impact | ASTM D1709 | 65 g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.