Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 2577 | 0.20to0.30 % |
| melt mass-flow rate | | ISO 1133 | 8.0 g/10min |
| density | | ISO 1183 | 1.25 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | | 内部方法 | HB |
| UL flame retardant rating | | 内部方法 | HB |
| burning rate | | FMVSS302 | 35 mm/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 5200 MPa |
| Tensile strain | Break | ISO 527-2 | 4.0 % |
| tensile strength | Break | ISO 527-2 | 70.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 12 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 7.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| dielectric strength | | IEC 60243-1 | 33 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | | Pass |
| vicat | | ISO 306/B50 | 134 °C |
| vicat | | ISO 306/A50 | 140 °C |
| Heat distortion temperature | | ISO 75-2/A | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare