ABS Mablex 319 Entec Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Entec Polymers/Mablex 319 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | Entec Polymers/Mablex 319 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | 1.00mm,在油中 | IEC 60243-1 | 33 kV/mm |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| Mechanical properties | Test Condition | Test Method | Entec Polymers/Mablex 319 |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2 | 70.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
| Flexural modulus | ISO 178 | 5200 MPa |
| flammability | Test Condition | Test Method | Entec Polymers/Mablex 319 |
|---|---|---|---|
| burning rate | FMVSS302 | 35 mm/min | |
| UL flame retardant rating | 3.2mm | 内部方法 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | 1.6mm | 内部方法 | HB |
| physical property | Test Condition | Test Method | Entec Polymers/Mablex 319 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.20to0.30 % | |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 8.0 g/10min |
| density | ISO 1183 | 1.25 g/cm³ |
| Thermal performance | Test Condition | Test Method | Entec Polymers/Mablex 319 |
|---|---|---|---|
| vicat | BallPressureTest(75°C) | Pass | |
| -- | ISO 306/A50 | 140 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 125 °C |
| vicat | -- | ISO 306/B50 | 134 °C |