Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.16 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 60.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 200 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| burning rate | | FMVSS302 | + |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISOType | | ISO 1874 | PA6.MHRZ.14-080.CF10 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 42 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 3.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 8000 MPa |
| tensile strength | Yield | ISO 527-2/5 | 130 MPa |
| Tensile strain | Break | ISO 527-2/5 | 4.5 % |
| Flexural modulus | | ISO 178 | 6700 MPa |
| bending strength | | ISO 178 | 195 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+08 ohms |
| Volume resistivity | | IEC 60093 | 1E+08 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 190 °C |
| vicat | | ISO 306/B | 200 °C |
| melting temperature | | ISO 11357-3 | 221 °C |
| Short term use temperature | | | <200 °C |
| TEMPERATURE | | | 110 °C |
| TEMPERATURE | | | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.