PA6 Tarnamid® T- 27 CF10 Grupa Azoty ATT Polymers GmbH
--
Mining applications
Filler, carbon fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 3.5 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 42 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 3.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| ISOType | ISO 1874 | PA6.MHRZ.14-080.CF10 |
| hardness | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 200 MPa |
| Electrical performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+08 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+08 ohms |
| Mechanical properties | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 130 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 4.5 % |
| Flexural modulus | ISO 178 | 6700 MPa | |
| Tensile modulus | ISO 527-2/1 | 8000 MPa | |
| bending strength | ISO 178 | 195 MPa |
| flammability | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB | |
| burning rate | FMVSS302 | + |
| physical property | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.30 % |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 60.0 cm³/10min |
| density | ISO 1183 | 1.16 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.90 % |
| Thermal performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T- 27 CF10 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| vicat | ISO 306/B | 200 °C | |
| TEMPERATURE | 20000hr | 110 °C | |
| Short term use temperature | <200 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 190 °C |
| TEMPERATURE | 5000hr | 120 °C |