PC LNP™ LUBRICOMP™ DCP36 compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.40 g/cm³ | |
| ASTM D792 | 1.39 g/cm³ | ||
| Shrinkage rate | ASTM D955 | 0.17 % | |
| ASTM D955 | 0.30 % | ||
| Water absorption rate | ASTM D570 | 0.050 % | |
| ISO 62 | 0.10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| coefficient of friction | ASTM D3702Modified | 0.50 | |
| ASTM D3702Modified | 0.48 | ||
| Wear factor | ASTM D3702Modified | 0.650 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ISO 527-2/1 | 15300 MPa | |
| tensile strength | Break | ASTM D638 | 111 MPa |
| Break | ISO 527-2/5 | 120 MPa | |
| elongation | Break | ASTM D638 | 1.2 % |
| Tensile strain | Break | ISO 527-2/5 | 1.7 % |
| Flexural modulus | ASTM D790 | 13400 MPa | |
| ISO 178 | 13800 MPa | ||
| bending strength | ISO 178 | 183 MPa | |
| ASTM D790 | 186 MPa | ||
| ASTM D790 | 185 MPa | ||
| Wear factor | ASTM D3702Modified | 18.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTM D638 | 16300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 91 J/m | |
| ISO 180/1A | 8.7 kJ/m² | ||
| ASTM D4812 | 460 J/m | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 23 kJ/m² | |
| Dart impact | ASTM D3763 | 13.8 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.90 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 140 °C | |
| ISO 75-2/Bf | 145 °C | ||
| ASTM D648 | 137 °C | ||
| ISO 75-2/Af | 140 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 5E-06 cm/cm/°C | |
| ASTM D696 | 3.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.