Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.17 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | | ASTM D955 | 5.0to8.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 108 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D638 | 60 % |
| Flexural modulus | | ASTM D790 | 2160 MPa |
| bending strength | | ASTM D790 | 78.5 MPa |
| tensile strength | | ASTM D638 | 51.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 440 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 34 kV/mm |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Resistance | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 2 |
| dielectric constant | | ASTM D150 | 3.00 |
| Dissipation Factor | | ASTM D150 | 9E-03 |
| arc resistance | | ASTM D495 | 100 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 104 °C |
| RTI Elec | | UL 746 | 60.0 °C |
| RTI Elec | | UL 746 | 85.0 °C |
| RTI Elec | | UL 746 | 85.0 °C |
| RTI Elec | | UL 746 | 85.0 °C |
| RTI Imp | | UL 746 | 60.0 °C |
| RTI Imp | | UL 746 | 75.0 °C |
| RTI Imp | | UL 746 | 75.0 °C |
| RTI Imp | | UL 746 | 75.0 °C |
| RTI Str | | UL 746 | 60.0 °C |
| RTI Str | | UL 746 | 75.0 °C |
| RTI Str | | UL 746 | 75.0 °C |
| RTI Str | | UL 746 | 75.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.