PC Lupoy® GP5006AF LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 440 J/m |
| hardness | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 60 % |
| bending strength | 3.20mm | ASTM D790 | 78.5 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 2160 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 51.0 MPa |
| Electrical performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 34 kV/mm | |
| arc resistance | 3.00mm | ASTM D495 | PLC6 |
| High arc combustion index (HAI) | 1.7mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.7mm | UL 746 | PLC 3 |
| Dissipation Factor | 1MHz | ASTM D150 | 9E-03 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | UL 746 | PLC 2 |
| arc resistance | 1.59mm | ASTM D495 | 100 sec |
| High Voltage Arc Resistance | 3.00mm | UL 746 | PLC 4 |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.7mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 6.0 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 5.0to8.0 % |
| density | ASTM D792 | 1.17 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5006AF |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 104 °C |
| RTI Str | 0.75mm | UL 746 | 75.0 °C |
| RTI Imp | 1.7mm | UL 746 | 75.0 °C |
| RTI Elec | -- | UL 746 | 60.0 °C |
| RTI Imp | -- | UL 746 | 60.0 °C |
| RTI Elec | 3.0mm | UL 746 | 85.0 °C |
| RTI Imp | 3.0mm | UL 746 | 75.0 °C |
| RTI Elec | 0.75mm | UL 746 | 85.0 °C |
| RTI Imp | 0.75mm | UL 746 | 75.0 °C |
| RTI Elec | 1.7mm | UL 746 | 85.0 °C |
| RTI Str | 3.0mm | UL 746 | 75.0 °C |
| 1.7mm | UL 746 | 75.0 °C | |
| -- | UL 746 | 60.0 °C |