Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.19 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 23 g/10min |
| Shrinkage rate | | ASTM D955 | 0.24to3.9 % |
| Water absorption rate | Saturation | ASTM D750 | 0.74 % |
| average molecular weight | | 内部方法 | 258000 Mw |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 84 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.41 |
| tensile strength | Break | ASTM D1708 | 54.9 MPa |
| tensile strength | | ASTM D1708 | 4.11 MPa |
| tensile strength | | ASTM D1708 | 5.87 MPa |
| tensile strength | | ASTM D1708 | 24.2 MPa |
| elongation | Break | ASTM D1708 | 500 % |
| Flexural modulus | | ASTM D790 | 19.2 MPa |
| bending strength | | ASTM D790 | 0.945 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 64.8 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 4.16 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTME1356 | 162 °C |
| Glass Transition Temperature | | ASTME1356 | -8.00 °C |
| vicat | | ASTM D1525 | 82.5 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.