PC+TPU II 80A DSM Additive Manufacturing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
hardness | Test Condition | Test Method | DSM Additive Manufacturing/ II 80A |
---|---|---|---|
Shore hardness | 邵氏A | ASTM D2240 | 84 |
Electrical performance | Test Condition | Test Method | DSM Additive Manufacturing/ II 80A |
---|---|---|---|
dielectric constant | 60Hz | ASTM D150 | 4.16 |
dielectric strength | ASTM D149 | 17 kV/mm |
Mechanical properties | Test Condition | Test Method | DSM Additive Manufacturing/ II 80A |
---|---|---|---|
tensile strength | 100%应变 | ASTM D1708 | 5.87 MPa |
coefficient of friction | 与自身-动态 | ASTM D1894 | 0.41 |
Flexural modulus | ASTM D790 | 19.2 MPa | |
tensile strength | 300%应变 | ASTM D1708 | 24.2 MPa |
bending strength | 5.0%应变 | ASTM D790 | 0.945 MPa |
tensile strength | 50%应变 | ASTM D1708 | 4.11 MPa |
断裂 | ASTM D1708 | 54.9 MPa | |
elongation | 断裂 | ASTM D1708 | 500 % |
physical property | Test Condition | Test Method | DSM Additive Manufacturing/ II 80A |
---|---|---|---|
Water absorption rate | 饱和 | ASTM D750 | 0.74 % |
Shrinkage rate | MD | ASTM D955 | 0.24to3.9 % |
density | ASTM D792 | 1.19 g/cm³ | |
melt mass-flow rate | ASTM D1238 | 23 g/10min | |
average molecular weight | 内部方法 | 258000 Mw |
elastomer | Test Condition | Test Method | DSM Additive Manufacturing/ II 80A |
---|---|---|---|
tear strength | ASTM D624 | 64.8 kN/m |
Thermal performance | Test Condition | Test Method | DSM Additive Manufacturing/ II 80A |
---|---|---|---|
vicat | ASTM D1525 | 82.5 °C | |
Glass Transition Temperature | ASTME1356 | -8.00 °C | |
melting temperature | ASTME1356 | 162 °C |