Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 高耐磨级 |
| processability | Test Condition | Test Method | Test Result |
|---|
| process temperature | | | 170 °C |
| process temperature | | | 190 °C |
| process temperature | | | 180 °C |
| process temperature | | | 180-210 °C |
| screw speed | | | 80-120 rpm |
| Temperature | | | 60-80 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 2200 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 67 kg/cm²(MPa)[Lb/in²] |
| elongation at break | | ASTM D638/ISO 527 | 15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257/IEC 60093 | 1.E+16 Ω |
| Volume resistivity | | ASTM D257/IEC 60093 | 1.E+12 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.51 |
| Shrinkage rate | | ASTM D955 | 2.1 % |
| Water absorption rate | | ASTM D570/ISO 62 | 0.18 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Combustibility (rate) | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.