POM FL2020 MITSUBISHI ENGINEERING JAPAN
Iupital™
Casters
wear resistant、enhance、filling
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2020 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.E+16 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.E+12 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2020 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 67 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2200 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 2400 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 15 % |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2020 |
|---|---|---|---|
| characteristic | 高耐磨级 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2020 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 2.1 % | |
| density | ASTM D792/ISO 1183 | 1.51 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.18 % |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2020 |
|---|---|---|---|
| process temperature | 180-210 °C | ||
| screw speed | 80-120 rpm | ||
| Temperature | 60-80 °C |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/FL2020 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB |