PC Iupilon® ML-300

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.20 g/cm³
melt mass-flow rate		ISO 1133	16 g/10min
Melt volume flow rate		ISO 1133	15.0 cm³/10min
Shrinkage rate			0.50to0.70 %
	Shrinkage rate			0.50to0.70 %
	Shrinkage rate	Shrinkage rate			0.24 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	2500 MPa
tensile strength	Yield	ISO 527-2	62.0 MPa
Tensile strain	Yield	ISO 527-2	6.6 %
Nominal tensile fracture strain		ISO 527-2	120 %
Flexural modulus		ISO 178	2300 MPa
bending strength		ISO 178	91.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	64 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
dielectric strength		IEC 60243-1	31 kV/mm
dielectric strength	dielectric strength		IEC 60243-1	17 kV/mm
relative permittivity		IEC 60250	3.10
Surface Resistivity		IEC 60093	4E+15 ohms
Volume resistivity		IEC 60093	3E+16 ohms·cm
relative permittivity		IEC 60250	3.10
Dissipation Factor		IEC 60250	7E-04
Dissipation Factor	Dissipation Factor		IEC 60250	9E-03

Thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ISO 11359-2	6.3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	7.3E-05 cm/cm/°C
Heat distortion temperature		ISO 75-2/B	139 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	124 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.