PC Iupilon® ML-300 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® ML-300
Charpy Notched Impact Strength23°CISO 17964 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® ML-300
dielectric strength3.00mmIEC 60243-117 kV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602507E-04
dielectric strength1.00mmIEC 60243-131 kV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600934E+15 ohms
Dissipation Factor1MHzIEC 602509E-03
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® ML-300
Nominal tensile fracture strainISO 527-2120 %
Tensile modulusISO 527-22500 MPa
Tensile strain屈服ISO 527-26.6 %
tensile strength 屈服ISO 527-262.0 MPa
Flexural modulusISO 1782300 MPa
bending strengthISO 17891.0 MPa
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® ML-300
Shrinkage rateTD:3.20mm0.50to0.70 %
吸水率(饱和,23°C)0.24 %
Melt volume flow rate300°C/1.2kgISO 113315.0 cm³/10min
Shrinkage rateMD:3.20mm0.50to0.70 %
densityISO 11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO 113316 g/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupilon® ML-300
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B139 °C
1.8MPa,未退火，HDTISO 75-2/A124 °C
Linear coefficient of thermal expansionMDISO 11359-26.3E-05 cm/cm/°C
TDISO 11359-27.3E-05 cm/cm/°C