Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 55.0 cm³/10min |
| Shrinkage rate | | ISO 2577 | 0.70 % |
| Shrinkage rate | | ISO 2577 | 0.30 % |
| Shrinkage rate | | ISO 2577 | 0.40 % |
| Shrinkage rate | | ISO 2577 | 0.20 % |
| Water absorption rate | | ISO 62 | 0.40 % |
| density | | ISO 1183 | 1.39 g/cm³ |
| Apparent density | | ISO 60 | 0.80 g/cm³ |
| Water absorption rate | | ISO 62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 150 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO 7792 | PBT+PET+ASA.GHMR.09-060.GF15 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 50 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| Flexural modulus | | ISO 178/A | 5200 MPa |
| bending strength | | ISO 178/A | 150 MPa |
| Bending Strain | | ISO 178/A | 3.2 % |
| Tensile modulus | | ISO 527-2/1 | 6000 MPa |
| tensile strength | | ISO 527-2/5 | 100 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 210 °C |
| Heat distortion temperature | | ISO 75-2/A | 150 °C |
| vicat | | ISO 306/B120 | 165 °C |
| melting temperature | | ISO 11357-3 | 225to250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.