PBT+ASA POCAN® TP 740-101 000000 LANXESS GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
Suspended wall beam without notch impact strength23°CISO 180/1U40 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU50 kJ/m²
-30°CISO 179/1eU40 kJ/m²
Supplementary InformationTest ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
ISO ShortcutISO 7792PBT+PET+ASA.GHMR.09-060.GF15
hardnessTest ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
ball-indentation hardnessISO 2039-1150 MPa
Mechanical propertiesTest ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
Tensile strain断裂,23°CISO 527-2/52.5 %
Bending Strain23°CISO 178/A3.2 %
tensile strength 断裂,23°CISO 527-2/5100 MPa
bending strength23°CISO 178/A150 MPa
Flexural modulus23°CISO 178/A5200 MPa
Tensile modulus23°CISO 527-2/16000 MPa
flammabilityTest ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
UL flame retardant rating0.8mmUL 94HB
1.6mmUL 94HB
physical property Test ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
Shrinkage rateMD:120°C,4小时,2.00mm3ISO 25770.20 %
TD:270°C,2.00mm2ISO 25770.70 %
density23°CISO 11831.39 g/cm³
Melt volume flow rate270°C/5.0kgISO 113355.0 cm³/10min
Apparent densityISO 600.80 g/cm³
Water absorption rate平衡,23°C,50%RHISO 620.10 %
饱和,23°CISO 620.40 %
Shrinkage rateMD:270°C,2.00mm2ISO 25770.40 %
TD:120°C,4小时,2.00mm3ISO 25770.30 %
Thermal performanceTest ConditionTest MethodLANXESS GERMANY/POCAN® TP 740-101 000000
melting temperatureISO 11357-3225to250 °C
vicatISO 306/B120165 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B210 °C
1.8MPa,未退火，HDTISO 75-2/A150 °C