Technical Data Sheet
Test Condition | Test Method | Test Result | |
---|---|---|---|
density | ASTM D792 | 0.898to1.07 g/cm³ | |
ISO 1183 | 0.886to1.09 g/cm³ | ||
melt mass-flow rate | ASTM D1238 | 1.0to15 g/10min | |
ISO 1133 | 3.4to8.0 g/10min | ||
Melt volume flow rate | ISO 1133 | 10.9to12.1 cm³/10min | |
Shrinkage rate | ASTM D955 | 0.60to0.68 % | |
ISO 294-4 | 0.50to2.4 % | ||
Shore hardness | ASTM D2240 | 47to92 | |
ISO 868 | 39to91 | ||
Flexural modulus | ASTM D790 | 1330to1800 MPa | |
ISO 178 | 1380to2460 MPa | ||
bending strength | ISO 178 | 16.5to76.5 MPa | |
ASTM D790 | 24.4to54.0 MPa | ||
tensile strength | ISO 37 | 1.80to5.38 MPa | |
ASTM D638 | 1.03to33.4 MPa | ||
ISO 37 | 1.70to6.90 MPa | ||
ASTM D412 | 2.00to4.57 MPa | ||
ISO 37 | 1.00to8.00 MPa | ||
ISO 37 | 1.70to33.0 MPa | ||
Haze ratio | ASTM D1003 | 0.20to3.1 % | |
tensile strength | ISO 527-2 | 4.00to51.0 MPa | |
ISO 527-2 | 14.0to64.0 MPa | ||
Tensile strain | ISO 527-2 | 2.0to2.1 % | |
ASTM D638 | 30to260 % | ||
Nominal tensile fracture strain | ISO 527-2 | 2.5to500 % | |
tensile strength | ASTM D412 | 3.96to20.3 MPa | |
elongation | ASTM D412 | 550to850 % | |
ISO 37 | 400to890 % | ||
tear strength | ASTM D624 | 19.8to104 kN/m | |
ISO 34-1 | 18to110 kN/m | ||
compression set | ISO 815 | 18to36 % | |
Charpy Notched Impact Strength | ISO 179 | 1.6to9.9 kJ/m² | |
Impact strength of cantilever beam gap | ASTM D256 | 20to110 J/m | |
Dart impact | ASTM D3763 | 0.602to41.6 J | |
Maximum continuous use temperature | SAEJ2236 | 150to170 °C | |
Heat distortion temperature | ASTM D648 | 59.6to62.7 °C | |
brittle temperature | ASTM D746 | -60.0--59.0 °C | |
vicat | ASTM D1525 | 62.7to90.0 °C | |
ISO 306 | 62.0to93.5 °C | ||
burning rate | ISO 3795 | 37to54 mm/min | |
transmissivity | ASTM D1003 | 88.9to93.1 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.