Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt Volume Flow Rate (MVR) | | ISO 1133 | 9 cm³/10 min |
| Melt Mass Flow Rate (MFR) 300 ℃/1.2 kg | | ASTM D1238 | 10 g/10min |
| Longitudinal shrinkage rate (Flow) | | Internal | 0.4~0.8 |
| Shrinkage rate (Across Flow) | | Internal | 0.4~0.8 |
| Water absorption rate | | ISO 62 | 0.12 |
| Moisture absorption rate | | ISO 62 | 0.09 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|
| Vicat softening temperature | | ASTM D1525 | 141 °C |
| Vicat softening temperature | | ISO 306 | 142 °C |
| Vicat softening temperature | | ISO 306 | 141 °C |
| Relative Temperature Index (RTI) impact w/impact- | | UL 746B | 120 °C |
| Relative Temperature Index (RTI) Electrical Elec- | | UL 746B | 130 °C |
| Relative Temperature Index (RTI) intensity w/o impact- | | UL 746B | 130 °C |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness L | | ISO 2039-2 | 89 L |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmittance | | ASTM D1003 | 82 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength yield (yld) | | ASTM D638 | 58 Mpa |
| Tensile strength yield (yld) | | ISO 527 | 57 Mpa |
| Tensile strength fracture (brk) | | ISO 527 | 61 Mpa |
| Tensile strength fracture (brk) | | ASTM D638 | 64 Mpa |
| | ASTM D638 | 5.8 % |
| | ISO 527 | 5.5 % |
| | ASTM D638 | 131.4 % |
| | ISO 527 | 124.9 % |
| | ASTM D790 | 94 Mpa |
| | ISO 178 | 90 Mpa |
| Flexural modulus | | ISO 178 | 2150 Mpa |
| Flexural modulus | | ASTM D790 | 2210 Mpa |
| Tensile modulus | | ASTM D638 | 22610 Mpa |
| Tensile modulus | | ISO 527 | 2350 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched -30 ℃ (-22 ℉) | | ISO 179/1eA | 60 kJ/m² |
| Charpy Notched at 23 ℃ (73 ℉) | | ISO 179/1eA | 70 kJ/m² |
| Izod Notched on Cantilever Beam | | ASTM D256 | 795 J/m |
| Izod Unnotched -30 ℃ (-22 ℉) | | ISO 180/1A | 55 kJ/m² |
| Izod Notched at 23 ℃ (73 ℉) | | ASTM D256 | 890 J/m |
| | ISO 180/1A | 65 kJ/m² |
| Cantilever beam without notch (Izod Unnotched) 23 ℃ (73 ℉) | | ISO 180/1U | NB J/m |
| Instrumented dart impact energy -30 ℃ (-22 ℉) total energy | | ASTM D3763 | 85 J |
| | ASTM D3763 | 82 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.