Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1413T BK10296 SABIC INNOVATIVE KOREA
LEXAN™
Electronic and electrical accessories,Lighting applications,lens,Plastic bag,Electrical appliances
Middle flow,Short molding cycle,High ductility at low tem
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/1413T BK10296 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 80*10*3，23℃ | ISO 180/1U | NB J/m |
| Charpy Notched Impact Strength | V-notch Edgew，23℃ | ISO 179/1eA | 70 kJ/m² |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | 80*10*3 | ASTM D3763 | 82 J |
| Suspended wall beam without notch impact strength | 80*10*3，-30℃ | ISO 180/1A | 55 kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 890 J/m |
| Instrumented dart impact energy -30 ℃ (-22 ℉) total energy | 80*10*3 | ASTM D3763 | 85 J |
| Charpy Notched Impact Strength | V-notch Edgew，-30℃ | ISO 179/1eA | 60 kJ/m² |
| Suspended wall beam without notch impact strength | 80*10*3，23℃ | ISO 180/1A | 65 kJ/m² |
| Impact strength of cantilever beam gap | /，30℃ | ASTM D256 | 795 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE KOREA/1413T BK10296 |
|---|---|---|---|
| Hardness (Rockwell L) | ISO 2039-2 | 89 L |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE KOREA/1413T BK10296 |
|---|---|---|---|
| elongation | 50 mm/m，屈服 | ISO 527 | 5.5 % |
| Flexural modulus | 1.3 mm/min | ASTM D790 | 2210 Mpa |
| elongation at break | 50 mm/m | ISO 527 | 124.9 % |
| elongation | Type I, 5，屈服 | ASTM D638 | 5.8 % |
| tensile strength | 50 mm/m，断裂 | ISO 527 | 61 Mpa |
| bending strength | 1.3 mm/min/，屈服 | ASTM D790 | 94 Mpa |
| tensile strength | Type I, 5，屈服 | ASTM D638 | 58 Mpa |
| Tensile modulus | 50 mm/ | ASTM D638 | 22610 Mpa |
| elongation at break | Type I, 5 | ASTM D638 | 131.4 % |
| Flexural modulus | 2 mm/mi | ISO 178 | 2150 Mpa |
| Tensile modulus | 1 mm/ | ISO 527 | 2350 Mpa |
| tensile strength | 50 mm/m，屈服 | ISO 527 | 57 Mpa |
| Type I, 50，断裂 | ASTM D638 | 64 Mpa | |
| bending strength | 2 mm/，屈服 | ISO 178 | 90 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/1413T BK10296 |
|---|---|---|---|
| transmittance | 2.54 mm | ASTM D1003 | 82 % |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE KOREA/1413T BK10296 |
|---|---|---|---|
| RTI Imp | UL 746B | 130 °C | |
| vicat | Rate A/ | ASTM D1525 | 141 °C |
| Rate B/1 | ISO 306 | 141 °C | |
| RTI Elec | UL 746B | 130 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE KOREA/1413T BK10296 |
|---|---|---|---|
| Water absorption rate | 23°C/sat | ISO 62 | 0.12 |
| melt mass-flow rate | /，300℃/1.2 kg | ASTM D1238 | 10 g/10min |
| Water absorption rate | 23°C / 50 | ISO 62 | 0.09 |
| Shrinkage rate | 3.2 mm，Across Flow | Internal | 0.4-0.8 |
| 3.2 mm，Flow | Internal | 0.4-0.8 | |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 9 cm³/10 min |