Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.59 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| Shrinkage rate | | 内部方法 | 0.20to0.30 % |
| Water absorption rate | | ISO 62 | 0.050 % |
| GranuleHumidity | | | <0.030 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/50 | 1.6 % |
| Flexural modulus | | ISO 178 | 11000 MPa |
| bending strength | | ISO 178 | 150 MPa |
| Tensile modulus | | ISO 527-2/1 | 12300 MPa |
| tensile strength | Break | ISO 527-2/50 | 105 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 42 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 70 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 85 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 235 °C |
| Continuous use temperature | | IEC 60216 | 150 °C |
| vicat | | ISO 306/B50 | 237 °C |
| ball-indentation hardness | | IEC 60695-10-2 | 通过 |
| melting temperature | | ISO 11357-3 | 256 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare