PET TAROLOX 111 G6 Y0 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 111 G6 Y0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 85 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 42 kJ/m² |
| Impact strength of cantilever beam gap | -20°C | ASTM D256 | 70 J/m |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 111 G6 Y0 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 11000 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 1.6 % |
| Tensile modulus | ISO 527-2/1 | 12300 MPa | |
| bending strength | ISO 178 | 150 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 105 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 111 G6 Y0 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 111 G6 Y0 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.2mm | UL 94 | V-0 | |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 775 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 111 G6 Y0 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.20to0.30 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.050 % |
| GranuleHumidity | <0.030 % | ||
| Shrinkage rate | TD | 内部方法 | 0.50to0.70 % |
| density | ISO 1183 | 1.59 g/cm³ |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 111 G6 Y0 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 256 °C | |
| Continuous use temperature | IEC 60216 | 150 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| vicat | ISO 306/B50 | 237 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 235 °C |
| ball-indentation hardness | 245°C | IEC 60695-10-2 | 通过 |