Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.05 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 8.0 g/10min |
| melt mass-flow rate | | ASTMD1238 | 2.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.60 % |
| Water absorption rate | | ASTMD570 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 109 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | AS/NZS60695 | 550 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTMD790 | 78.0 MPa |
| tensile strength | | ASTMD638 | 48.0 MPa |
| elongation | | ASTMD638 | 35 % |
| Flexural modulus | | ASTMD790 | 2400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 200 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD696 | 8E-05 cm/cm/°C |
| | ASTMD648 | 84.0 °C |
| | ASTMD648 | 92.0 °C |
| | ASTMD648 | 100 °C |
| vicat | | ASTMD15254 | 114 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.