Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

ABS ABS X15 MARPLEX AUSTRALIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | MARPLEX AUSTRALIA/ ABS X15 |
---|---|---|---|
Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 200 J/m |
hardness | Test Condition | Test Method | MARPLEX AUSTRALIA/ ABS X15 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 109 |
Mechanical properties | Test Condition | Test Method | MARPLEX AUSTRALIA/ ABS X15 |
---|---|---|---|
bending strength | 3.20mm | ASTM D790 | 78.0 MPa |
elongation | 断裂,3.20mm | ASTM D638 | 35 % |
tensile strength | 3.20mm | ASTM D638 | 48.0 MPa |
Flexural modulus | 3.20mm | ASTM D790 | 2400 MPa |
flammability | Test Condition | Test Method | MARPLEX AUSTRALIA/ ABS X15 |
---|---|---|---|
Hot filament ignition temperature | 1.6mm | AS/NZS60695 | 550 °C |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | MARPLEX AUSTRALIA/ ABS X15 |
---|---|---|---|
Shrinkage rate | MD:3.00mm | ASTM D955 | 0.60 % |
Water absorption rate | 24hr | ASTM D570 | 0.25 % |
melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 2.0 g/10min |
density | ASTM D792 | 1.05 g/cm³ | |
melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 8.0 g/10min |
Thermal performance | Test Condition | Test Method | MARPLEX AUSTRALIA/ ABS X15 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 92.0 °C |
vicat | ASTM D15254 | 114 °C | |
Heat distortion temperature | 1.8MPa,未退火,12.7mm,HDT | ASTM D648 | 100 °C |
Linear coefficient of thermal expansion | MD | ASTM D696 | 8E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 84.0 °C |