ABS A120
33
- Properties:Antistatic
- Certificates:UL
CompareTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 抗静电 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | JIS K-7210 | 41 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D-638 | 46 Mpa | |
| elongation at break | ASTM D-638 | 40 % | |
| bending strength | ASTM D-790 | 76 Mpa | |
| Flexural modulus | ASTM D-790 | 2450 Mpa | |
| Impact strength of cantilever beam gap | ASTM D-256 | 108 J/m | |
| tensile strength | ASTM D638/ISO 527 | 40 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2450 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 76 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 108 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 46 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.05 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 41 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D-1525 | 103 °C | |
| Heat distortion temperature | ASTM D-648 | 81 °C | |
| combustibility | UL 94 | HB | |
| Heat distortion temperature | ASTM D648/ISO 75 | 81 ℃（℉） | |
| vicat | ASTM D1525/ISO R306 | 103 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.