ABS A120 ASAHI JAPAN
--
--
Antistatic
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Basic performance | Test Condition | Test Method | ASAHI JAPAN/A120 |
---|---|---|---|
melt mass-flow rate | JIS K-7210 | 41 g/10min |
Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/A120 |
---|---|---|---|
bending strength | ASTM D790/ISO 178 | 76 kg/cm²(MPa)[Lb/in²] | |
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 108 kg·cm/cm(J/M)ft·lb/in | |
tensile strength | 断裂 | ASTM D-638 | 46 Mpa |
Flexural modulus | ASTM D790/ISO 178 | 2450 kg/cm²(MPa)[Lb/in²] | |
ASTM D-790 | 2450 Mpa | ||
bending strength | ASTM D-790 | 76 Mpa | |
Impact strength of cantilever beam gap | ASTM D-256 | 108 J/m | |
elongation at break | ASTM D638/ISO 527 | 46 % | |
ASTM D-638 | 40 % | ||
tensile strength | ASTM D638/ISO 527 | 40 kg/cm²(MPa)[Lb/in²] |
other | Test Condition | Test Method | ASAHI JAPAN/A120 |
---|---|---|---|
characteristic | 抗静电 |
Physical properties | Test Condition | Test Method | ASAHI JAPAN/A120 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.05 | |
melt mass-flow rate | ASTM D1238/ISO 1133 | 41 g/10min |
Thermal performance | Test Condition | Test Method | ASAHI JAPAN/A120 |
---|---|---|---|
Heat distortion temperature | HDT | ASTM D-648 | 81 °C |
combustibility | 1/8" | UL 94 | HB |
Heat distortion temperature | HDT | ASTM D648/ISO 75 | 81 ℃(℉) |
vicat | ASTM D1525/ISO R306 | 103 ℃(℉) | |
ASTM D-1525 | 103 °C |