Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.10 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 90to100 |
| Barcol Hardness | | ASTM D2583 | 48to52 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HotFormingTemperature | | 内部方法 | 177to193 °C |
| CyclesFreeze-Thaw | | 内部方法 | NoEffect |
| HotFormingTemperature | | 内部方法 | 149to171 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2410 MPa |
| tensile strength | | ASTM D638 | 42.1 MPa |
| elongation | | ASTM D638 | 6.2 % |
| Flexural modulus | | ASTM D790 | 2310 MPa |
| Flexural modulus | | ASTM D790 | 2230 MPa |
| bending strength | | ASTM D790 | 61.4 MPa |
| bending strength | | ASTM D790 | 73.8 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 170 J/m |
| Dart impact | | 内部方法 | 73.2 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 89.4 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare