Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.13 g/cm³ |
Melt volume flow rate | | ISO 1133 | 113 cm³/10min |
Shrinkage rate | | ISO 294-4 | 0.80 % |
Shrinkage rate | | ISO 294-4 | 0.70 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2/2 | 3470 MPa |
tensile strength | Yield | ISO 527-2/1A/50 | 84.0 MPa |
Tensile strain | Yield | ISO 527-2/1A/50 | 3.6 % |
Tensile strain | Break | ISO 527-2/1A/50 | 13 % |
Flexural modulus | | ISO 178 | 2700 MPa |
bending strength | | ISO 178 | 103 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/A | 3.8 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/A | 4.8 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 190 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 180 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 3.5 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 4.6 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | DIN 53482 | 1E+15 ohms·cm |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/B | 175 °C |
Heat distortion temperature | | ISO 75-2/A | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.