Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 12 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Water absorption rate | | ASTMD570 | 0.15 % |
| Water absorption rate | | ASTMD570 | 0.32 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 73 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.586 |
| transmissivity | | ASTM D1003 | 85.0 % |
| Haze ratio | | ASTM D1003 | 1.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 100 MPa |
| bending strength | | ISO 178 | 95.8 MPa |
| Abrasion | | ASTM D1044 | 45 % |
| Tensile modulus | | ASTM D638 | 2270 MPa |
| Tensile modulus | | ISO 527-2/50 | 2300 MPa |
| tensile strength | | ASTM D638 | 64.3 MPa |
| tensile strength | Yield | ISO 527-2/50 | 65.2 MPa |
| tensile strength | | ASTM D638 | 69.1 MPa |
| tensile strength | Break | ISO 527-2/50 | 69.6 MPa |
| elongation | | ASTM D638 | 6.3 % |
| elongation | Yield | ISO 527-2/50 | 6.1 % |
| elongation | | ASTM D638 | 150 % |
| elongation | Break | ISO 527-2/50 | 150 % |
| Flexural modulus | | ASTM D790 | 2200 MPa |
| Flexural modulus | | ISO 178 | 2300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 750 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 65 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTMD256 | 无断裂 |
| Dart impact | | ASTM D3763 | 86.9 J |
| Impact strength of cantilever beam gap | | ASTM D1822 | 378 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Volume resistivity | | ASTM D257 | 2E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 3.00 |
| dielectric constant | | ASTM D150 | 3.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 121 °C |
| Heat distortion temperature | | ISO 75-2/A | 123 °C |
| Heat distortion temperature | | ASTM D648 | 125 °C |
| vicat | | ISO 306/B50 | 141 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 134 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare