PC 2081-12 Trinseo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 750 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTMD256 | 无断裂 |
| Dart impact | 23°C,总能量 | ASTM D3763 | 86.9 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² | |
| 23°C | ISO 180/A | 65 kJ/m² |
| hardness | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 73 |
| R级 | ASTM D785 | 118 |
| Electrical performance | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 1E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| Volume resistivity | ASTM D257 | 2E+17 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 2E-03 |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| dielectric strength | ASTMD149 | 17 kV/mm |
| Mechanical properties | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| tensile strength | 屈服2 | ASTM D638 | 64.3 MPa |
| elongation | 断裂2 | ASTM D638 | 150 % |
| 断裂 | ISO 527-2/50 | 150 % | |
| Flexural modulus | --3 | ASTM D790 | 2200 MPa |
| Abrasion | ASTM D1044 | 45 % | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.2 MPa |
| bending strength | --3 | ASTM D790 | 100 MPa |
| elongation | 屈服2 | ASTM D638 | 6.3 % |
| 屈服 | ISO 527-2/50 | 6.1 % | |
| bending strength | --4,5 | ISO 178 | 95.8 MPa |
| Tensile modulus | -- | ISO 527-2/50 | 2300 MPa |
| --2 | ASTM D638 | 2270 MPa | |
| tensile strength | 断裂2 | ASTM D638 | 69.1 MPa |
| 断裂 | ISO 527-2/50 | 69.6 MPa | |
| Flexural modulus | --4,5 | ISO 178 | 2300 MPa |
| optical performance | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| transmissivity | ASTM D1003 | 85.0 % | |
| Haze ratio | ASTM D1003 | 1.0 % |
| physical property | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ASTMD570 | 0.32 % |
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| MD | ISO 294-4 | 0.50to0.70 % | |
| density | ASTMD792 | 1.20 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.15 % |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/2081-12 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 121 °C |
| 1.8MPa,退火，HDT | ASTM D648 | 125 °C | |
| vicat | ISO 306/B50 | 141 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 123 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 134 °C |