Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Outdoor applicability | | UL 746C | f1 |
| Water absorption rate | | ISO 62 | 0.15 % |
| Water absorption rate | | ISO 62 | 0.35 % |
| Shrinkage rate - Flow 2 | | 内部方法 | 0.50 到 0.70 % |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 21.0 cm3/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO 2039-1 | 95.0 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.586 |
| transmissivity | | ASTM D1003 | 88.0 到 90.0 % |
| Haze ratio | | ASTM D1003 | < 0.80 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| | ISO 180/1U | 无断裂 |
| Suspended wall beam notch impact strength 6 | | ISO 180/1A | 65 kJ/m² |
| | ISO 180/1U | 无断裂 |
| Suspended wall beam notch impact strength 6 | | ISO 180/1A | 11 kJ/m² |
| Simply supported beam without notch impact strength 5 | | ISO 179/1eU | 无断裂 |
| Simply supported beam without notch impact strength 5 | | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | 内部方法 | 10.0 mg |
| Bending modulus 3 | | ISO 178 | 2300 Mpa |
| | ISO 178 | 90.0 Mpa |
| Tensile strain | | ISO 527-2/50 | 100 % |
| Tensile strain | | ISO 527-2/50 | 6.0 % |
| Tensile stress | | ISO 527-2/50 | 63.0 Mpa |
| Tensile stress | | ISO 527-2/50 | 65.0 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2350 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| Processing (melt) temperature | | | 280 到 300 °C |
| Temperature at the rear of the barrel | | | 260 到 280 °C |
| Temperature in the middle of the barrel | | | 270 到 290 °C |
| Temperature at the front of the material cylinder | | | 280 到 300 °C |
| Spray nozzle temperature | | | 270 到 290 °C |
| Temperature | | | 80 到 100 °C |
| drying temperature | | | 120 °C |
| drying time | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Hopper temperature | | | 60 到 80 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | > 1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 KV/mm |
| | IEC 60250 | 2.70 |
| | IEC 60250 | 2.70 |
| | IEC 60250 | 2.70 |
| Dissipation Factor | | IEC 60250 | 1.0E-3 |
| Dissipation Factor | | IEC 60250 | 1.0E-3 |
| Dissipation Factor | | IEC 60250 | 0.010 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI | | UL 746 | 130 °C |
| RTI Elec | | UL 746 | 130 °C |
| thermal conductivity | | ISO 8302 | 0.20 W/m/K |
| Ball Pressure Test | | IEC 60695-10-2 | 通过 |
| | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Ball Pressure Test | | IEC 60695-10-2 | 通过 |
| vicat | | ISO 306/B50 | 140 °C |
| vicat | | ISO 306/B120 | 141 °C |
| | ISO 75-2/Be | 133 °C |
| | ISO 75-2/Ae | 122 °C |
| RTI Imp | | UL 746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.