Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| Water absorption rate | | ISO 62 | 0.50 % |
| Water absorption rate | | ISO 62 | 14 % |
| Water absorption rate | | ISO 62 | 38.0 mg |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 105 |
| ball-indentation hardness | | ISO 2039-1 | 375 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ISO 4589-2 | 58 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1B/1 | 5800 MPa |
| tensile strength | Break | ISO 527-2/1B/5 | 140 MPa |
| Tensile strain | Break | ISO 527-2/1B/5 | 3.0 % |
| compression stress | | ISO 604/1 | 42.0 MPa |
| compression stress | | ISO 604/1 | 82.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+13 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+14 ohms·cm |
| relative permittivity | | IEC 60250 | 3.20 |
| Dissipation Factor | | IEC 60250 | 1E-03 |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| relative permittivity | | IEC 60250 | 3.30 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.40 W/m/K |
| Continuous use temperature | | | 310 °C |
| Continuous use temperature | | | 500 °C |
| Continuous use temperature | | | 425 °C |
| Heat distortion temperature | | ISO 75-2/A | 425 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.