Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBI Quadrant EPP CELAZOLE® PBI Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.5 kJ/m² |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| ball-indentation hardness | 10.0mm | ISO 2039-1 | 375 MPa |
| Rockwell hardness | E计秤,10.0mm | ISO 2039-2 | 105 |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+14 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| relative permittivity | 100Hz | IEC 60250 | 3.30 |
| 1MHz | IEC 60250 | 3.20 | |
| dielectric strength | 1.00mm | IEC 60243-1 | 22 kV/mm |
| Surface Resistivity | IEC 60093 | >1.0E+13 ohms |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1B/1 | 5800 MPa | |
| Tensile strain | 断裂 | ISO 527-2/1B/5 | 3.0 % |
| tensile strength | 断裂 | ISO 527-2/1B/5 | 140 MPa |
| compression stress | 1%应变 | ISO 604/1 | 42.0 MPa |
| 2%应变 | ISO 604/1 | 82.0 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 58 % |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 14 % |
| density | ISO 1183 | 1.30 g/cm³ | |
| Water absorption rate | 23°C,24hr,3.00mm | ISO 62 | 0.50 % |
| 23°C,3.00mm | ISO 62 | 38.0 mg |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP CELAZOLE® PBI |
|---|---|---|---|
| Continuous use temperature | 玻璃转化温度 | 425 °C | |
| Linear coefficient of thermal expansion | MD：23到150°C | 2.5E-05 cm/cm/°C | |
| Continuous use temperature | --3 | 310 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 425 °C |
| Continuous use temperature | --4 | 500 °C | |
| Linear coefficient of thermal expansion | MD：23到100°C | 2.5E-05 cm/cm/°C | |
| MD：导热系数(23°C) | 0.40 W/m/K | ||
| MD：>150°C | 2.5E-05 cm/cm/°C |