Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 2577 | 0.15to0.45 % |
| Water absorption rate | | ISO 62 | <0.20 % |
| Shrinkage rate | | ISO 2577 | <0.050 % |
| density | | ISO 1183 | 1.80to2.00 g/cm³ |
| Apparent density | | ISO 60 | 0.75to0.90 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO 527-2 | 10000to14000 MPa |
| tensile strength | Injection | ISO 527-2 | 80.0to90.0 MPa |
| Flexural modulus | Injection | ISO 178 | 11000to14000 MPa |
| bending strength | Injection | ISO 178 | 120to160 MPa |
| compression stress | | ISO 604 | 150to200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 3.5to4.5 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 7.0to10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 4.004.50 |
| Dissipation Factor | | IEC 60250 | 0.010to0.030 |
| Dissipation Factor | | IEC 60250 | 0.010to0.030 |
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14到1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 15to20 kV/mm |
| relative permittivity | | IEC 60250 | 4.505.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | >200 °C |
| Heat distortion temperature | | ISO 75-2/C | 130to150 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.0E-6到1.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90to1.1 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.