PA66 Amilan®  CM3004G30 B TORAY SHENZHEN

33
  • Properties:
    Flame retardantGlass fiber reinforced Glass fiber reinforced bFiller: Glass fiber reinfFlame retardant grade30%Filler by weighthalogen-containing Flame retardant grade30% filler by weighthalogen-containing
  • Usages:
    Office suppliesAutomotive sectorbuilding materialsElectronic fieldElectrical field
  • Compare View Prices

Technical Data Sheet

Other performanceTest ConditionTest MethodTest Result
filler content无水｜30 wt%
filler content1.3%水｜- wt%
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-40°CkJ/m²7.0 --
Charpy Notched Impact Strength23°CkJ/m²9.5 14
Impact strength of simply supported beam without notch23°CkJ/m²65 70
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.40mmV-0 --
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate23℃，24hrASTM D-570无水｜0.4 %
Water absorption rate23℃，24hrASTM D-5701.3%水｜- %
mechanical propertiesTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap23℃，Unnotched1/8无水｜65 kg.cm/cm
Impact strength of cantilever beam gap23℃，Unnotched1/81.3%水｜70 kg.cm/cm
tensile strength23℃，BreakASTM D-638无水｜1640 kg/cm2
tensile strength23℃，BreakASTM D-6381.3%水｜1350 kg/cm2
Elongation at Break23℃ASTM D-638无水｜5 %
Elongation at Break23℃ASTM D-6381.3%水｜5 %
bending strength23℃ASTM D-790无水｜2490 kg/cm2
bending strength23℃ASTM D-7901.3%水｜2000 kg/cm2
Bending modulus23℃ASTM D-790无水｜93200 kg/cm2
Bending modulus23℃ASTM D-7901.3%水｜65000 kg/cm2
Tensile strainBreak,-40°C%2.5 --
Tensile strainBreak,23°C%3.0 3.0
Tensile strainBreak,80°C%4.5 --
Bending modulus-40°CMPa10200 --
Bending modulus23°CMPa9300 6500
Bending modulus80°CMPa5500 --
bending strength-40°CMPa275 --
bending strength23°C250 MPa
bending strength80°CMPa150 --
Taber abraser1000Cyclesmg26.0 --
tensile strength-40°CMPa190 --
tensile strength23°C165 MPa
tensile strength80°CMPa110 --
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionASTM D-696无水｜2 10-5cm/cm.℃
Linear coefficient of thermal expansionASTM D-6961.3%水｜-
Hot deformation temperature18.6kg/cm2ASTM D-648无水｜251 °C
Hot deformation temperature18.6kg/cm2ASTM D-6481.3%水｜- °C
Melting temperature差示扫描测热计DSC法265 °C
UL-94 flame retardant gradeUL 94无水｜V-0
UL-94 flame retardant gradeUL 941.3%水｜-
Hot deformation temperature0.45MPa,Unannealed°C251 --
Melting temperature°C265 --
Linear coefficient of thermal expansionMDcm/cm/°C2E-05 --
Physical propertiesTest ConditionTest MethodTest Result
densityASTM D-792无水｜1.59
densityASTM D-7921.3%水｜-
density23°Cg/cm³1.59 --
Shrinkage rateTD:3.00mm3%0.60-0.90 --
Shrinkage rateMD:3.00mm4%0.20-0.50 --
Water absorption rate23°C,24hr%0.60 --
Water absorption rateSaturation,23°C%4.0 --
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityASTM D-2571.3%水｜8×1013 Ω.cm
Dielectric strength1/8"ASTM D-149无水｜38 KV/mm
Dielectric strength1/8"ASTM D-1491.3%水｜33 KV/mm
Compared to the Leakage Traceability Index (CTI)UL 746无水｜200 V
Compared to the Leakage Traceability Index (CTI)UL 7461.3%水｜- V
Dissipation factor106HzASTM D-150无水｜0.003-0.009
Dissipation factor106HzASTM D-1501.3%水｜-
Arc resistance1/8"ASTM D-495无水｜70-80 S
Arc resistance1/8"ASTM D-4951.3%水｜- S
Volume resistivityASTM D-257无水｜8×1014 Ω.cm
Volume resistivityohms·cm1E+15 1E+13
Dielectric strengthkV/mm38 33
Dielectric constant23°C,1kHz4.00 --
Dielectric constant23°C,1MHz0.0100 --
Arc resistancesec70.0 --
Compared to the anti leakage trace indexCTIVPLC 3
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-Sale,23°C121 --
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.