Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3004G30 B TORAY SHENZHEN
Amilan®
Office supplies、Automotive sector、building materials、Electronic field、Electrical field
Flame retardant、Glass fiber reinforced、 Glass fiber reinforced b、Filler: Glass fiber reinf、Flame retardant grade、30%、Filler by weight、halogen-containing 、Flame retardant grade、30% filler by weight、halogen-containing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| 1.3%水｜- wt% |
| Impact resistance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 65 70 |
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 -- |
| 23°C | kJ/m² | 9.5 14 |
| hardness | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 121 -- |
| Basic performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 1.3%水｜- % |
| Electrical performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| dielectric strength | 1/8" | ASTM D-149 | 1.3%水｜33 KV/mm |
| dielectric constant | 23°C,1MHz | 0.0100 -- | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | 200 -- |
| Volume resistivity | ASTM D-257 | 无水｜8×1014 Ω.cm | |
| dielectric strength | kV/mm | 38 33 | |
| Arc resistance 6 | sec | 70.0 -- | |
| arc resistance | 1/8" | ASTM D-495 | 1.3%水｜- S |
| Loss factor | 106Hz | ASTM D-150 | 1.3%水｜- |
| dielectric constant | 23°C,1kHz | 4.00 -- | |
| IEC Conductive Track Index | UL 746 | 1.3%水｜- V | |
| Volume resistivity | ohms·cm | 1E+15 1E+13 |
| Mechanical properties | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| Flexural modulus | -40°C | MPa | 10200 -- |
| 23°C | MPa | 9300 6500 | |
| Bending stress | 23°C | MPa | 250 |
| IZOD impact strength | 23℃，无缺口1/8 | 1.3%水｜70 kg.cm/cm | |
| 1000Cycles | mg | 26.0 -- | |
| Bending stress | -40°C | MPa | 275 -- |
| Tensile stress | -40°C | MPa | 190 -- |
| Tensile strain | 断裂,80°C | % | 4.5 -- |
| Bending stress | 80°C | MPa | 150 -- |
| 23℃ | ASTM D-790 | 1.3%水｜2000 kg/cm2 | |
| Tensile stress | 80°C | MPa | 110 -- |
| elongation at break | 23℃ | ASTM D-638 | 1.3%水｜5 % |
| Tensile strain | 断裂,23°C | % | 3.0 3.0 |
| Flexural modulus | 80°C | MPa | 5500 -- |
| Tensile fracture strength | 23℃ | ASTM D-638 | 1.3%水｜1350 kg/cm2 |
| Tensile stress | 23°C | MPa | 165 |
| flexural modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 kg/cm2 |
| Tensile strain | 断裂,-40°C | % | 2.5 -- |
| flammability | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | V-0 -- |
| physical property | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| Shrinkage rate | MD:3.00mm4 | % | 0.20到0.50 -- |
| density | ASTM D-792 | 1.3%水｜- | |
| Water absorption rate | 饱和,23°C | % | 4.0 -- |
| Shrinkage rate | TD:3.00mm3 | % | 0.60到0.90 -- |
| density | 23°C | g/cm³ | 1.59 -- |
| Water absorption rate | 23°C,24hr | % | 0.60 -- |
| Thermal performance | Test Condition | Test Method | TORAY SHENZHEN/CM3004G30 B |
|---|---|---|---|
| melting point | 差示扫描测热计DSC法 | 265 °C | |
| UL-94 flame retardant grade | UL 94 | 1.3%水｜- | |
| ASTM D-696 | 1.3%水｜- | ||
| MD | cm/cm/°C | 2E-05 -- | |
| melting temperature | °C | 265 -- | |
| 0.45MPa,未退火 | °C | 251 -- | |
| ASTM D-696 | 无水｜2 10-5cm/cm.℃ | ||
| heat deflection temperature | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- °C |