Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 8.0 g/10 min |
| Shrinkage rate - flow | | ASTM D955 | 0.20 到 0.60 % |
| Water absorption rate | | ASTM D570 | 0.12 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 75 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.550 |
| transmissivity | | ISO 13468-1 | 91.0 % |
| transmissivity | | ISO 13468-1 | 82.0 % |
| Haze ratio | | ISO 14782 | < 0.50 % |
| Haze ratio | | ISO 14782 | 6.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC 60695-11-10, -20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 3100 Mpa |
| Tensile stress | | ISO 527-2/5 | 62.0 Mpa |
| Tensile strain | | ISO 527-2/5 | 3.0 % |
| Bending modulus 3 | | ISO 178 | 3100 Mpa |
| Bending stress 3 | | ISO 178 | 100 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | < 80 °C |
| Drying time - hot air dryer | | | 3.0 到 4.0 hr |
| Temperature at the rear of the barrel | | | 210 到 240 °C |
| Temperature in the middle of the barrel | | | 210 到 240 °C |
| Temperature at the front of the material cylinder | | | 210 到 240 °C |
| Processing (melt) temperature | | | 210 到 240 °C |
| Temperature | | | 50 到 70 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/A | 90.0 °C |
| vicat | | ISO 306/B50 | 95.0 °C |
| | ASTM D696 | 6.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.