Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.50to1.60 g/cm³ |
| Apparent density | | ISO 60 | 0.55to0.75 g/cm³ |
| Shrinkage rate | | ISO 2577 | 0.80to1.2 % |
| Shrinkage rate | | ISO 2577 | 0.50to0.90 % |
| Water absorption rate | | ISO 62 | <2.0 % |
| Shrinkage rate | | ISO 2577 | 0.80to1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 900 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Compression molding pressure | | | >20.0 MPa |
| Compression molding temperature | | | 160to180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | Compression Molded | ISO 178 | 7000to9000 MPa |
| Flexural modulus | Injection | ISO 178 | 7000to9000 MPa |
| bending strength | Compression Molded | ISO 178 | 90.0to120 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 5000to8000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 5000to8000 MPa |
| tensile strength | | ISO 527-2 | 45.0to60.0 MPa |
| tensile strength | Injection | ISO 527-2 | 50.0to70.0 MPa |
| bending strength | Injection | ISO 178 | 100to130 MPa |
| compression stress | | ISO 604 | 200to250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 6.0to9.0 kJ/m² |
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 1.2to1.8 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 1.4to2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 4.5to7.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+11到1.0E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 15to20 kV/mm |
| relative permittivity | | IEC 60250 | 11.016.0 |
| relative permittivity | | IEC 60250 | 7.009.00 |
| Dissipation Factor | | IEC 60250 | 0.30to0.50 |
| Dissipation Factor | | IEC 60250 | 0.030to0.050 |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | ASTME1461 | 0.50to0.60 W/m/K |
| maximum service temperature | | IEC 60216 | 160 °C |
| maximum service temperature | | IEC 60216 | 135 °C |
| Heat distortion temperature | | ISO 75-2/A | 155to180 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/C | 110to130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.