Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Phenolic MELOPAS® MP 180 RASCHIG GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
Impact strength of simply supported beam without notch注塑ISO 179/1eU6.0to9.0 kJ/m²
模压成型ISO 179/1eU4.5to7.0 kJ/m²
Charpy Notched Impact Strength模压成型ISO 179/1eA1.2to1.8 kJ/m²
注塑ISO 179/1eA1.4to2.0 kJ/m²
Supplementary InformationTest ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
Compression molding pressure>20.0 MPa
Compression molding temperature160to180 °C
Electrical performanceTest ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
dielectric strengthIEC 60243-115to20 kV/mm
Volume resistivityIEC 600931.0E+11到1.0E+12 ohms·cm
relative permittivity100HzIEC 6025011.016.0
Dissipation Factor100HzIEC 602500.30to0.50
arc resistanceASTM D495PLC 5
relative permittivity1MHzIEC 602507.009.00
Surface ResistivityIEC 600931.0E+10到1.0E+11 ohms
Dissipation Factor1MHzIEC 602500.030to0.050
Mechanical propertiesTest ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
tensile strength CompressionMoldedISO 527-245.0to60.0 MPa
bending strength注塑ISO 178100to130 MPa
Flexural modulus注塑ISO 1787000to9000 MPa
compression stressISO 604200to250 MPa
Tensile modulus模压成型ISO 527-25000to8000 MPa
Flexural modulus模压成型ISO 1787000to9000 MPa
tensile strength 注塑ISO 527-250.0to70.0 MPa
bending strength模压成型ISO 17890.0to120 MPa
Tensile modulus注塑ISO 527-25000to8000 MPa
flammabilityTest ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
Hot filament ignition temperatureIEC 60695-2-13900 °C
UL flame retardant rating1.5mmUL 94V-0
Burning wire flammability indexIEC 60695-2-12960 °C
physical property Test ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
Shrinkage rateISO 25770.80to1.3 %
MD：--4ISO 25770.50to0.90 %
Apparent densityISO 600.55to0.75 g/cm³
Shrinkage rateMD：--3ISO 25770.80to1.2 %
Water absorption rate23°C,24hrISO 62<2.0 %
densityISO 11831.50to1.60 g/cm³
Thermal performanceTest ConditionTest MethodRASCHIG GmbH/MELOPAS® MP 180
maximum service temperature20,000hIEC 60216135 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A155to180 °C
Linear coefficient of thermal expansionMD：50到100°CISO 11359-21.5E-5到3.5E-5 cm/cm/°C
Heat distortion temperature8.0MPa,未退火，HDTISO 75-2/C110to130 °C
thermal conductivityASTME14610.50to0.60 W/m/K
maximum service temperature<50hIEC 60216160 °C