Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.5 % |
| Shrinkage rate | | ISO 294-4 | 1.7 % |
| melt mass-flow rate | | ISO 1133 | 20 g/10 min |
| Shrinkage rate | | ISO 294-4 | 1.3 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 63 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | 36 Mpa |
| elongation at break | | ISO 527 | 460 % |
| Flexural elasticity | | ISO 178 | 300 Mpa |
| Impact strength of cantilever beam gap | | ISO 179/IeA | PARTIAL BREAK kJ/㎡ |
| Volume resistivity | | IEC 60093 | 7.0E 13 Ohm cm |
| Volume resistivity | | IEC 60093 | 3.0E 13 Ohm |
| dielectric strength | | IEC 60243 | 17 KV/mm |
| Shore hardness | | ISO 868 | 63 |
| tensile strength | | ISO 527-2 | 40.0 Mpa |
| Tensile strain | | ISO 527-2 | 460 % |
| Flexural modulus | | ISO 178 | 350 Mpa |
| Charpy Notched Impact Strength | | ISO 179/1eA | 无断裂 |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527 | 36 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 2.8E+15 Ohm |
| Volume resistivity | | IEC 60093 | 6.3E+13 ohm·cm |
| dielectric strength | | IEC 60243-1 | 17 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 3146C | 211 °C |
| melt mass-flow rate | | ISO 1133 | 8 g/10 min |
| melting temperature | | ISO 3146 | 212 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.