TPEE 1163-201LL TAIWAN CHANGCHUN
LONGLITE®
Cable、Fitness equipment
Creep resistance、antioxidant、Fatigue resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TAIWAN CHANGCHUN/1163-201LL |
|---|---|---|---|
| Melting temperature (DSC) | ISO 3146 | 212 °C | |
| Melting Temperature | ISO 3146C | 211 °C | |
| Melt index | 2.16kg at 230℃ | ISO 1133 | 8 g/10 min |
| Physical | Test Condition | Test Method | TAIWAN CHANGCHUN/1163-201LL |
|---|---|---|---|
| Melt index | 230℃/2.16 kg | ISO 1133 | 20 g/10 min |
| hardness | 邵氏 D | ISO 868 | 63 |
| Moisture Absorption | 24hr | ISO 62 | 0.5 % |
| Modeling Shrinkage | ISO 294-4 | 1.3 % | |
| Moisture Absorption | 23℃, 24 hr | ISO 62 | 0.30 % |
| Mechanical Properties | Test Condition | Test Method | TAIWAN CHANGCHUN/1163-201LL |
|---|---|---|---|
| Tensile Strain | 断裂 | ISO 527-2 | 460 % |
| Volume Resistivity | IEC 60093 | 7.0E 13 Ohm cm | |
| Tensile strength | ISO 527 | 36 Mpa | |
| Surface Resistivity | IEC 60093 | 3.0E 13 Ohm | |
| Insulation failure strength | IEC 60243 | 17 KV/mm | |
| hardness | 邵氏 D | ISO 868 | 63 |
| Impact Strength | ISO 179/IeA | PARTIAL BREAK kJ/㎡ | |
| Flexural Modulus | ISO 178 | 350 Mpa | |
| Tensile Elongation | ISO 527 | 460 % | |
| Tensile Stress | 屈服 | ISO 527-2 | 40.0 Mpa |
| Charpy Notched Impact Strength | ISO 179/1eA | 无断裂 | |
| Flexural Strength | ISO 178 | 300 Mpa |
| Other | Test Condition | Test Method | TAIWAN CHANGCHUN/1163-201LL |
|---|---|---|---|
| Tensile strength | ISO 527 | 36 Mpa |
| Electrical Properties | Test Condition | Test Method | TAIWAN CHANGCHUN/1163-201LL |
|---|---|---|---|
| Volume Resistivity | IEC 60093 | 6.3E+13 ohm·cm | |
| Arc Resistance | 2.00 mm | IEC 60243-1 | 17 KV/mm |
| Surface Resistivity | IEC 60093 | 2.8E+15 Ohm |