Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | DIN 53479 | 1.13 g/cm³ |
| melt mass-flow rate | | DIN 53735 | 5.0to8.0 g/10min |
| Shrinkage rate | | DIN 53464 | 1.0E-3-0.014 % |
| Water absorption rate | | DIN 53495 | 1.8 % |
| Water absorption rate | | DIN 53495 | 8.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | DIN 53453 | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | DIN 53455 | 70.0 MPa |
| Tensile strain | Break | DIN 53452 | 70 % |
| Flexural modulus | | DIN 53457 | 1980 MPa |
| bending strength | | DIN 53457 | 105 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| dielectric strength | | DIN 53481 | 20 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | DIN 53461 | 160 °C |
| Heat distortion temperature | | DIN 53461 | 62.0 °C |
| Heat distortion temperature | Melting Temperature | DIN 53461 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.