PA Sup-tech B103F Shanghai Suptech Engineering Plastics Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| Charpy Notched Impact Strength | DIN 53453 | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 118 |
| Electrical performance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| dielectric strength | DIN 53481 | 20 kV/mm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| Mechanical properties | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| Tensile strain | 断裂 | DIN 53452 | 70 % |
| tensile strength | 断裂 | DIN 53455 | 70.0 MPa |
| Flexural modulus | DIN 53457 | 1980 MPa | |
| bending strength | DIN 53457 | 105 MPa |
| flammability | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| density | DIN 53479 | 1.13 g/cm³ | |
| melt mass-flow rate | DIN 53735 | 5.0to8.0 g/10min | |
| Shrinkage rate | DIN 53464 | 1.0E-3-0.014 % | |
| Water absorption rate | 饱和,23°C | DIN 53495 | 8.5 % |
| 23°C,24hr | DIN 53495 | 1.8 % |
| Thermal performance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech B103F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | DIN 53461 | 62.0 °C |
| 熔融温度，HDT | DIN 53461 | 220 °C | |
| 0.45MPa,未退火，HDT | DIN 53461 | 160 °C |